鋁/鋼沉頭開口型抽芯鉚釘
作者： 點擊量：次
材質
鉚體: 5056 Alu.Alloy
釘芯: Steel 表面顏色
鉚體: Polished
釘芯: Zinc Plated
鋁/鋼沉頭開口型抽芯鉚釘尺寸標注示意圖：
鋁/鋼沉頭開口型抽芯鉚釘規格尺寸表：
鉚體: 5056 Alu.Alloy
釘芯: Steel 表面顏色
鉚體: Polished
釘芯: Zinc Plated
鋁/鋼沉頭開口型抽芯鉚釘尺寸標注示意圖：
鋁/鋼沉頭開口型抽芯鉚釘規格尺寸表：
|
D1 NOM. |
DRILL NO. &HOLE SIZE | ART. CODE | GRIP RANGE | L (MAX) |
D NOM. |
K MAX |
P MIN. |
SHEAR LBS |
TENSILE LBS |
||
| INCH | MM | INCH | MM | ||||||||
|
3/32" 2.44mm |
#41 2.5-2.6 |
5-AS32 C | 0.079-0.125 | 2.0-3.2 | 0.250 | 6.4 |
0.174" 4.4 |
0.027" 0.69 |
1.00" 25.4 |
90 400N |
120 535N |
| 5-AS34 C | 0.126-0.250 | 3.2-6.4 | 0.375 | 9.5 | |||||||
| 5-AS36 C | 0.251-0.375 | 6.4-9.5 | 0.500 | 12.7 | |||||||
|
1/8" 3.2mm |
#30 3.3-3.4
|
5-AS42 C | 0.092-0.125 | 2.3-3.2 | 0.275 | 7.0 |
0.220" 5.6 |
0.031" 0.79 |
1.06" 27 |
170 760N |
220 980N |
| 5-AS43 C | 0.126-0.187 | 3.2-4.8 | 0.337 | 8.6 | |||||||
| 5-AS44 C | 0.188-0.250 | 4.8-6.4 | 0.400 | 10.2 | |||||||
| 5-AS45 C | 0.251-0.312 | 6.4-7.9 | 0.462 | 11.7 | |||||||
| 5-AS46 C | 0.313-0.375 | 7.9-9.5 | 0.525 | 13.3 | |||||||
| 5-AS48 C | 0.313-0.500 | 9.5-12.7 | 0.650 | 16.5 | |||||||
|
5/32" 4.0mm |
#20 4.1-4.2 |
5-AS53 C | 0.120-0.187 | 3.0-4.8 | 0.362 | 9.2 |
0.281" 7.1 |
0.040" 1.02 |
1.06" 27 |
260 1160N |
350 1560N |
| 5-AS54 C | 0.188-0.250 | 4.8-6.4 | 0.425 | 10.8 | |||||||
| 5-AS56 C | 0.251-0.375 | 6.4-9.5 | 0.550 | 14.0 | |||||||
| 5-AS58C | 0.376-0.500 | 9.5-12.7 | 0.675 | 17.1 | |||||||
|
3/16" 4.8mm |
#11 4.9-5.0 |
5-AS63 C | 0.151-0.187 | 3.8-4.8 | 0.387 | 9.8 |
0.348" 8.8 |
0.050" 1.27 |
1.06" 27 |
380 1700N |
500 2230N |
| 5-AS64 C | 0.188-0.250 | 4.8-6.4 | 0.450 | 11.4 | |||||||
| 5-AS66 C | 0.251-0.375 | 6.4-9.5 | 0.575 | 14.6 | |||||||
| 5-AS68 C | 0.376-0.500 | 9.5-12.7 | 0.700 | 17.8 | |||||||
| 5-AS610 C | 0.501-0.625 | 12.7-19.5 | 0.825 | 21.0 | |||||||
|
1/4" 6.4mm |
F 6.5-6.6 |
5-AS84 C | 0.125-0.250 | 3.2-6.4 | 0.500 | 12.7 |
0.470" 11.9 |
0.060" 1.52 |
1.25" 321 |
700 3120N |
920 4100N |
| 5-AS86 C | 0.251-0.375 | 6.4-9.5 | 0.625 | 15.9 | |||||||
| 5-AS88C | 0.376-0.500 | 9.5-12.7 | 0.750 | 19.1 | |||||||